| Quantity: | |
|---|---|
| GB | ISO | ASTM | JIS |
| TU1 | Cu-OF | C10200 | C1020 |
| T2 | Cu-RTP | C11000 | C1100 |
| TP1 | Cu-DLP | C12000 | C1201 |
| TP2 | Cu-DHP | C12200 | C1220 |
| GB | Composition(%) | |||
| Cu | P | O | Other | |
| TU1 | 99.97 | 0.002 | less than 0.002 | balance |
| T2 | 99.9 | - | - | balance |
| TP1 | 99.9 | 0.004-0.012 | - | balance |
| TP2 | 99.9 | 0.015-0.040 | - | balance |
| ASTM | Composition(%) | |||
| Cu | P | O | Other | |
| C10200 | 99.95 | 0.001-0.005 | - | balance |
| C11000 | 99.9 | - | - | balance |
| C12000 | 99.9 | 0.004-0.012 | - | balance |
| C12200 | 99.9 | 0.015-0.040 | - | balance |
| Grade | Temper | Thickness /mm | Elongation | Hardness | ||
| A11.2/% | Thickness/mm | HV | ||||
| T2 | C1100 | M20 | 4-14 | no less than 30 | - | - |
| TP1 TP2 | C1201 C1220 | 60 | 0.3-10 | no less than 30 | noless than 0.3 | no more than 70 |
| TU1 | C1020 | H01 | no less than 25 | 60-95 | ||
| H02 | no less than 8 | 80-110 | ||||
| H04 | - | 90-120 | ||||
| H06 | - | no less than 110 | ||||
| GB | ISO | ASTM | JIS |
| TU1 | Cu-OF | C10200 | C1020 |
| T2 | Cu-RTP | C11000 | C1100 |
| TP1 | Cu-DLP | C12000 | C1201 |
| TP2 | Cu-DHP | C12200 | C1220 |
| GB | Composition(%) | |||
| Cu | P | O | Other | |
| TU1 | 99.97 | 0.002 | less than 0.002 | balance |
| T2 | 99.9 | - | - | balance |
| TP1 | 99.9 | 0.004-0.012 | - | balance |
| TP2 | 99.9 | 0.015-0.040 | - | balance |
| ASTM | Composition(%) | |||
| Cu | P | O | Other | |
| C10200 | 99.95 | 0.001-0.005 | - | balance |
| C11000 | 99.9 | - | - | balance |
| C12000 | 99.9 | 0.004-0.012 | - | balance |
| C12200 | 99.9 | 0.015-0.040 | - | balance |
| Grade | Temper | Thickness /mm | Elongation | Hardness | ||
| A11.2/% | Thickness/mm | HV | ||||
| T2 | C1100 | M20 | 4-14 | no less than 30 | - | - |
| TP1 TP2 | C1201 C1220 | 60 | 0.3-10 | no less than 30 | noless than 0.3 | no more than 70 |
| TU1 | C1020 | H01 | no less than 25 | 60-95 | ||
| H02 | no less than 8 | 80-110 | ||||
| H04 | - | 90-120 | ||||
| H06 | - | no less than 110 | ||||